| Grade | Chemical composition（%） | Thickness (mm) |
|||
| GB | ASTM | EN | Cu | Zr | 0.08-3.0 |
| TZr0.1 | C15100 | CuZr0.1 | ≥99.8 | 0.05-0.15 | |
| Physical properties | ||||||
| Density (g/cm³) |
Modulus of elasticity (GPa) |
Thermal expansion coefficient (×10-6/K) |
Electrical conductivity (%IACS) |
Thermal conductivity W(m·K) |
||
| 8.9 | 121 | 17.6 | 90 | 350 | ||
| Mechanical properties | Bend properties | |||||
| Temper | Hardness HV |
Tension test | 90°R/T(Thick＜0.8mm) | |||
| Tensile Strength Rm/MPa |
Yield Strength MPa |
Elongation % |
Good way | Bad way | ||
| H01 | 80-110 | 280-320 | ≥180 | ≥22 | 0 | 0 |
| H02 | 90-120 | 300-360 | ≥240 | ≥15 | 0.5 | 0.5 |
| H03 | 100-130 | 330-390 | ≥310 | ≥8 | 1 | 1 |
| H04 | 110-140 | 370-430 | ≥350 | ≥4 | 1.5 | 1.5 |
| H06 | 120-150 | 410-460 | ≥395 | ≥2 | 2 | 2 |
| H08 | ≥140 | 440-500 | ≥420 | ≥1 | 2.5 | 2.5 |