| GB | ISO | ASTM | JIS |
| TU1 | Cu-OF | C10200 | C1020 |
| T2 | Cu-ETP | C11000 | C1100 |
| TP1 | Cu-DLP | C12000 | C1201 |
| TP2 | Cu-DHP | C12200 | C1220 |
| GB | Composition(%) | ||||
| Cu | P | O | Other | ||
| TU1 | 99.97 | 0.002 | less than 0.002 | balance | |
| T2 | 99.9 | - | - | balance | |
| TP1 | 99.9 | 0.004-0.012 | - | balance | |
| TP2 | 99.9 | 0.015-0.040 | - | balance | |
| ASTM | Composition(%) | ||||
| Cu | P | O | Other | ||
| C10200 | 99.95 | 0.001-0.005 | - | balance | |
| C11000 | 99.9 | - | - | balance | |
| C12000 | 99.9 | 0.004-0.012 | - | balance | |
| C12200 | 99.9 | 0.015-0.040 | - | balance | |
| Grade（China） | Grade（Japan） | Temper | Thickness/mm | Tensile Strength Rm(N/mm2) | Elongation A1 1.3% | Hardness HV |
| T2 T3 TU1 TU2 TP1 TP2 | C1100 C1020 C1220 | O60 | more than 0.15 | no less than 195 | no less than 30 | no less than 70 |
| H01 | 215-295 | no less than 25 | 60-95 | |||
| H02 | 245-345 | no less than 8 | 80-110 | |||
| H04 | 295-395 | no less than 3 | 90-120 | |||
| H06 | no less than 350 | no less than 110 |
| Classification/um | 12 | 18 | 35 | |
| Width/mm | 520 | 520 | 520 | |
| Purity(%) | ≧99.9 | |||
| Density(g/m³) | 8.89 | |||
| Area Weight(g/㎡) | 107±3 | 160±5 | 311±6 | |
| Tensile Strength(N/㎜²) | Normal | ≧0.5 | ≧1.0 | ≧1.0 |
| 180℃30Min | ≧5 | ≧7 | ≧10 | |
| Roughness | Ra(μm) | ≦0.35 | ||
| Rz(μm) | ≦2 | |||
| Anti-oxidization | 200℃,≧90Minnondiscolouring | |||
| temperature85℃,humidity85%,nondiscolouring | ||||
| Solder Resistance | 288℃/10S no bubbles | |||
| Peel Strength(N/㎜) | ≧1.0 | ≧1.0 | ≧1.0 | |
| Surface Quality | No wrinkles, no color difference, no scratches, no convex and concave points | |||
| Storage Condition | Temperature0℃≦t≦25℃,RH≦60%,90 days | |||
| Chemical Resistance(%) | ≦5 | |||
Product Description
|
GB
|
ISO
|
ASTM
|
JIS
|
|
TU1、TU2
|
Cu-OF
|
C10200
|
C1020
|
|
T2
|
Cu-RTP
|
C11000
|
C1100
|
|
TP1
|
Cu-DLP
|
C12000
|
C1201
|
|
TP2
|
Cu-DHP
|
C12200
|
C1220
|
|
GB
|
Composition(%)
|
||||
|
Cu
|
P
|
O
|
Other
|
||
|
TU1
|
99.97
|
0.002
|
less than 0.002
|
balance
|
|
|
TU2
|
99.95
|
0.002
|
less than 0.003
|
balance
|
|
|
T2
|
99.9
|
－
|
-
|
balance
|
|
|
TP1
|
99.9
|
0.004-0.012
|
-
|
balance
|
|
|
TP2
|
99.9
|
0.015-0.040
|
-
|
balance
|
|
|
ASTM
|
Composition(%)
|
||||
|
Cu
|
P
|
O
|
Other
|
||
|
C10200
|
99.95
|
0.001-0.005
|
-
|
balance
|
|
|
C11000
|
99.9
|
－
|
-
|
balance
|
|
|
C12000
|
99.9
|
0.004-0.012
|
-
|
balance
|
|
|
C12200
|
99.9
|
0.015-0.040
|
-
|
balance
|
|
|
Mechanical properties of the strip
|
|||||||
|
Grade
（China）
|
Grade
（Japan） |
Temper
|
Thickness/mm
|
Tensile Strength Rm/(N/mm2）
|
Elongation
Al 1.3/% |
Hardness HV
|
|
|
Copper
strip |
M
|
more than
0.2 |
more than
195 |
more than
30 |
less than 70
|
||
|
T2 T3
|
C1100
|
Y4
|
215-275
|
more than 25
|
60-90
|
||
|
TU1 TU2
|
C1020
|
Y2
|
245-345
|
more than
8 |
80-110
|
||
|
TP1 TP2
|
C1201
C1220 |
Y
|
295-380
|
more than
3 |
90-120
|
||
|
T
|
more than
350 |
more than 110
|
|||||