Short Description:
C42300 belongs to a multi mechanism synergistic strengthening alloy, which precipitates precipitates in the Cu Sn Zn solid solution matrix through heat treatment to improve the overall performance of the alloy. Its stress relaxation resistance is superior to ordinary pure deformation strengthening alloys, with excellent bending performance, good strength, and good conductivity; This material is not sensitive to stress corrosion cracking and is a highly conductive alternative material to phosphorus bronze.
| Grade | Chemical composition（%）≤ | Thickness (mm) |
||||
| ASTM | Cu | Sn | Ni | Si | Zn | 0.1-2.0 |
| C42300 | 89 | 1 | 1 | 0.2 | Balance | |
| Physical properties | ||||||
| Density (g/cm³) |
Modulus of elasticity (GPa) |
Thermal expansion coefficient (×10-6/K) |
Electrical conductivity (%IACS) |
Thermal conductivity W(m·K) |
||
| 8.88 | 120 | 16.7 | 32 | 125 | ||
| Mechanical properties | Bend properties | |||||
| Temper | Vickers Hardness HV0.2 |
Tension test | 90°R/T(Thick≤0.5mm) | |||
| Tensile Strength （MPa） |
Yield Strength(MPa） | Elongation % （A50） |
Good way | Bad way | ||
| R440（1/2H） | 140-170 | 440-540 | ≥420 | ≥8 | 0 | 0 |
| R520（3/4H） | 150-190 | 520-620 | ≥500 | ≥6 | 0 | 0.5 |
| R560（H） | 170-210 | 560-660 | ≥550 | ≥3 | 0.5 | 1.5 |
| R620（EH） | 190-220 | 620-720 | ≥590 | ≥1 | 1 | 2 |
FAQ
Q: How long is your delivery time?
A: Generally it is within 15 days if the goods are in stock. or it is less than 30 days if the goods are not in stock, it is according to quantity.
Q: Do you provide samples ?
A: Yes, we could offer the sample.
Q: What ls your terms of payment?
A.30% T/T in advance ,balance before shipment. And the price depends on the material and the quantity.
If you have another question, please feel free to contact us.